PVC elevator belt has solid woven carcass as the core,put it into impregnated PVC paste resin to plastify under high temperature.
It is fire resistance and anti-static solid woven elevator belt.
PVC elevator belt has solid woven carcass as the core,put it into impregnated PVC paste resin to plastify under high temperature.It is fire resistance and anti-static solid woven elevator belt.
Features:
1. Solid woven carcass completely solve the problem of ply separation and belt delamination.
2. High resistance to oil, grease, chemicals, corrosion,flame, abrasion with anti-static properties.
3. Consists of tight woven carcass with resilient PVC cover. Prevent the bolts from penetrating the belt and secure the fixation between buckets and belt.
Flexibility allows the belt running along elevator pulley smoothly and avoid belt mistracking.
Belting:
Belting compounds range from standard Gr-2, Fire resistant, High Temp and MOR.
Base Belting tensions range from 120 PVC to over 1200 PIW for high capacity elevators.
Accessories:
We offer all needed hardware for bucket replacement and splicing.
Elevator bolt: Fang bolt, Euro bolt, Norway bolt.
Elevator pulley and tail: Rubber cover or lagging pad
Buckets:
Elevator buckets are available in a wide variety of materials,
including fabricated steel, ductile iron, nylon, HDPE and urethane.
Specification:
Type | Colour | Tensile Strength | Ambient | Elongation @10% | Environmental protection | Flame resistance | Conductivity |
(N/mm) | temperature(℃) | tensile Strength(%) | |||||
PVC480 | Green, Black | ≥480 | -15～+85 | 0.7 | operation | operation | √ |
PVC680 | ≥680 | 0.8 | operation | operation | √ | ||
PVC880 | ≥880 | 0.9 | operation | operation | √ | ||
PVC1080 | ≥1080 | 0.9 | operation | operation | √ | ||
PVC480 | White | ≥480 | -15～+85 | 0.7 | √ | operation | operation |
PVC680 | ≥680 | 0.8 | √ | operation | operation | ||
PVC880 | ≥880 | 0.9 | √ | operation | operation |
Cover Rubber Properties:
Items | Unit | Index Value |
Tensile Strength | Mpa | ≥15 |
Elongation @ Break | % | ≥300 |
Abrasion Loss | mm3 | ≤100 |
Conductivity | MQ | ≤300 |
Winding property | 200,000 times | without crack |
Hardness | Shore A | 70 |
Friction coefficient (with steel) | 0.68 |
PVC elevator belt has solid woven carcass as the core,put it into impregnated PVC paste resin to plastify under high temperature.It is fire resistance and anti-static solid woven elevator belt.
Features:
1. Solid woven carcass completely solve the problem of ply separation and belt delamination.
2. High resistance to oil, grease, chemicals, corrosion,flame, abrasion with anti-static properties.
3. Consists of tight woven carcass with resilient PVC cover. Prevent the bolts from penetrating the belt and secure the fixation between buckets and belt.
Flexibility allows the belt running along elevator pulley smoothly and avoid belt mistracking.
Belting:
Belting compounds range from standard Gr-2, Fire resistant, High Temp and MOR.
Base Belting tensions range from 120 PVC to over 1200 PIW for high capacity elevators.
Accessories:
We offer all needed hardware for bucket replacement and splicing.
Elevator bolt: Fang bolt, Euro bolt, Norway bolt.
Elevator pulley and tail: Rubber cover or lagging pad
Buckets:
Elevator buckets are available in a wide variety of materials,
including fabricated steel, ductile iron, nylon, HDPE and urethane.
Specification:
Type | Colour | Tensile Strength | Ambient | Elongation @10% | Environmental protection | Flame resistance | Conductivity |
(N/mm) | temperature(℃) | tensile Strength(%) | |||||
PVC480 | Green, Black | ≥480 | -15～+85 | 0.7 | operation | operation | √ |
PVC680 | ≥680 | 0.8 | operation | operation | √ | ||
PVC880 | ≥880 | 0.9 | operation | operation | √ | ||
PVC1080 | ≥1080 | 0.9 | operation | operation | √ | ||
PVC480 | White | ≥480 | -15～+85 | 0.7 | √ | operation | operation |
PVC680 | ≥680 | 0.8 | √ | operation | operation | ||
PVC880 | ≥880 | 0.9 | √ | operation | operation |
Cover Rubber Properties:
Items | Unit | Index Value |
Tensile Strength | Mpa | ≥15 |
Elongation @ Break | % | ≥300 |
Abrasion Loss | mm3 | ≤100 |
Conductivity | MQ | ≤300 |
Winding property | 200,000 times | without crack |
Hardness | Shore A | 70 |
Friction coefficient (with steel) | 0.68 |